An advanced, high build composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1 - 2 mm (40 - 80 mils) per coat. However, greater single coat film thickness is achievable when spray applied. Non-shrinking, 100% solids. Color is Light Gray.

 
ARC S1HB is a high viscosity, high performance composite lining that is designed to be spray applied but may also be applied by brush. ARC S1HB allows for uniform coverage over rough surfaces and yields excellent barrier properties for long-term corrosion and chemical resistance in immersion exposures. The cured ARC S1HB provides a barrier film with unrivaled adhesion and resistance to corrosion.

Technical Data

• Dry Temperature Dry (Min/Max)                               -20 F (-29C) to 175 F (80 C)
• Wet Temperature (Min/Max)                                     -20 F (-29C) to 125 F (52 C)
• Compressive Strength - kg/cm2 - Mpa (psi)         870 - 84 (12400)
• Flexural Strength - kg/cm2 - Mpa (psi)                   420 -41 (6,000)  
• Tensile Strength - kg/cm2/Mpa (psi)                      385 - 38 (5,550)  
• Tensile Adhesion - kg/cm2 - Mpa (psi)                  Greater than 28- 2,8 (400)
• Impact Resistance - nt m (in. lbs.)                          > Concrete
• Shore D Hardness                                                      85