A high gloss, self-leveling, quartz reinforced composite designed to protect  new concrete surfaces as well as to resurface and restore existing concrete  surfaces. FCS 305 has resistance to dilute concentrations of a broad  spectrum of chemicals. The product is self priming and can be applied at a  thickness as low as 2 mm (.08") up to 4 mm (.16") with fine aggregate blend  and up to 9 mm (.35") with a coarse blend

Technical Data

• Dry Temperature Dry (Min/Max)                                 -20 F (-29C) to 140 F (60 C) 
• Wet Temperature (Min/Max)                                       -20 F (-29C) to 140 F (60 C) 
• Compressive Strength - kg/cm2 - Mpa (psi)            806 - 79 (11,500) 
• Flexural Strength - kg/cm2 - Mpa (psi)                      277 - 27 (3900) 
• Tensile Strength - kg/cm2/Mpa (psi)                          527 - 52 (7,500) 
• Tensile Adhesion - kg/cm2 - Mpa (psi)                      Greater than 28- 2,8 (400) 
• Impact Resistance - nt m (in. lbs.)                              > Concrete 
• Shore D Hardness                                                          85