An advanced ceramic composite, with flowable viscosity, for the repair and  protection of all metal surfaces subjected to severe erosion, abrasion and  chemical attack. ARC MXC is formulated with a high concentration of ceramic beads and  fine ceramic particles for extremely abrasive environments where superior  protection is desirable. ARC MXC may be molded where close tolerances  in application and a smooth finish are necessary, or where accessibility is  limited. It can be hand troweled on horizontal surfaces at a  minimum thickness of 6 mm as well as poured into casting applications at  a minimum thickness of 9 mm (3/8”) or more.

 TECHNICAL DATA

• Dry Temperature Dry (Min/Max)                           -20 F (-29C) to 400 F (205 C)
• Wet Temperature (Min/Max)                                 -20 F (-29C) to 205 F (95 C)
• Compressive Strength - kg/cm2 - Mpa (psi)     1120 - 109 (15,900)
• Flexural Strength - kg/cm2 - Mpa (psi)               415 - 40 (5,900)
• Tensile Strength - kg/cm2/Mpa (psi)                   295 - 29 (4,200)
• Tensile Adhesion - kg/cm2 - Mpa (psi)               Greater than 123 - 12 (1,750)
• Impact Resistance - nt m (in. lbs.)                       9,1 (80)
• Shore D Hardness                                                   89